NIKROTHAL LX(ニクロタル LX)
体積抵抗率 [μΩm] |
抵抗温度係数 [×10-6/℃] |
---|---|
*1.33 | ±5,±10 |
密度 g/cm3 (20℃) |
融点 ℃ |
最高使用温度 ℃ |
---|---|---|
8.30 | 1390 | -55~+250 |
化学成分 | C | Si | Mn | Cr | Fe | Al | Ni | Cu |
---|---|---|---|---|---|---|---|---|
(%) | ≦0.02 | 0.5~0.7 | 2.1~2.3 | 18~20 | ≦0.1 | 2.4~2.6 | 残部(BAL) | 1.6~1.8 |
記 号 | 種 類 | 範囲 (mm) |
---|---|---|
NIKROTHAL LX | 線 | φ0.5~0.02 |
記号 | 体積抵抗率(23℃μΩm) |
---|---|
NIKROTHAL LX | 1.33 |
0.500 | 0.196 | ±5 | 6.77 | 614 | 1.63 | |
---|---|---|---|---|---|---|
0.475 | 0.177 | ±5 | 7.51 | 680 | 1.47 | |
0.450 | 0.159 | ±5 | 8.36 | 758 | 1.32 | |
0.425 | 0.142 | ±5 | 9.38 | 849 | 1.18 | |
0.400 | 0.126 | ±5 | 10.6 | 959 | 1.04 | |
0.375 | 0.110 | ±5 | 12.0 | 1091 | 0.917 | |
0.350 | 0.0962 | ±5 | 13.8 | 1252 | 0.799 | |
0.320 | 0.0804 | ±5 | 16.5 | 1498 | 0.668 | |
0.300 | 0.0707 | ±5 | 18.8 | 1704 | 0.587 | |
0.280 | 0.0616 | ±5 | 21.6 | 1957 | 0.511 | |
0.260 | 0.0531 | ±5 | 25.1 | 2269 | 0.441 | |
0.250 | 0.0491 | ±5 | 27.1 | 2454 | 0.407 | |
0.240 | 0.0452 | ±5 | 29.4 | 2663 | 0.375 | |
0.230 | 0.0415 | ±5 | 32.0 | 2900 | 0.345 | |
0.220 | 0.0380 | ±5 | 35.0 | 3169 | 0.316 | |
0.210 | 0.0346 | ±5 | 38.4 | 3479 | 0.287 | |
0.200 | 0.0314 | ±5 | 42.3 | 3835 | 0.261 | |
0.190 | 0.0284 | ±5 | 46.9 | 4249 | 0.235 | |
0.180 | 0.0254 | ±5 | 52.3 | 4735 | 0.211 | |
0.170 | 0.0227 | ±5 | 58.6 | 5308 | 0.188 | |
0.160 | 0.0201 | ±5 | 66.1 | 5992 | 0.167 | |
0.150 | 0.0177 | ±5 | 75.3 | 6818 | 0.147 | |
0.140 | 0.0154 | ±5 | 86.4 | 7827 | 0.128 | |
0.130 | 0.0133 | ±5 | 100 | 9077 | 0.110 | |
0.120 | 0.0113 | ±8 | 118 | 10653 | 0.0939 | |
0.110 | 0.00950 | ±8 | 140 | 12678 | 0.0789 | |
0.100 | 0.00785 | ±8 | 169 | 15340 | 0.0652 | |
0.090 | 0.00636 | ±8 | 209 | 18939 | 0.0528 | |
0.080 | 0.00503 | ±8 | 265 | 23969 | 0.0417 | |
0.070 | 0.00385 | ±8 | 346 | 31307 | 0.0319 | |
0.060 | 0.00283 | ±8 | 470 | 42612 | 0.0235 | |
0.050 | 0.00196 | ±8 | 677 | 61361 | 0.0163 | |
0.045 | 0.00159 | ±10 | 837 | 75754 | 0.0132 | |
0.040 | 0.00126 | ±10 | 1058 | 95876 | 0.0104 | |
0.035 | 0.000960 | ±10 | 1382 | 125226 | 0.00799 | |
0.030 | 0.000707 | ±10 | 1882 | 170447 | 0.00587 | |
0.028 | 0.000615 | ±10 | 2160 | 195666 | 0.00511 | |
0.025 | 0.000491 | ±10 | 2709 | 245443 | 0.00407 | |
0.022 | 0.000380 | ±10 | 3499 | 316946 | 0.00316 | |
0.020 | 0.000314 | ±10 | 4234 | 383505 | 0.00261 |